POLYOLEFIN FABRIC SPECIFICATIONS

Warranty: Five-Year Pro-Rated Warranty
Heavyweight fabric for applications requiring a flame retardant surface and UV stability, such as structures and alternate daily landfill covers. The scrim is produced in a special weaving pattern to enhance thickness, flatness, abrasion resistance, and tear properties.

FABRIC SPECIFICATIONS

WEAVE:
Nominal 16 by 22 ppi woven flame retardant HDPE scrim using natural FR / UV 1600 denier tapes

COATING:

2.75 mil. average each side

COLOR:

Off-white

WEIGHT:
11 ounce / yard

THICKNESS: 24 mils. – ASTM D5199

PERFORMANCE

GRAB TENSILE:
Warp 325 lb. 1445N Weft 450 lb. 2000 N

ASTM D5034

TONGUE TEAR:
Warp 145 lb. 645N Weft 140 lb. 622 N
ASTM D2261

MULLEN BURST:
730 psi 5037 kPa
ASTM D3786

ACCELERATED UV WEATHERING:

80% strength retention after 2000 hours
QUV (A-340 lamps) 8 hours UV @ 60 degree C;
4 hours condensation
@ 50 degree C

ASTM G53


LOW TEMPERATURE
                BEND:
Pass at 30 degree C
(-22 degree F) ASTM D522

FR & UV PERFORMANCE
This product meets the requirements of CPAI-84 (1995) Sect. 5 and 6, ASTM E84 (Class 1), NFPA 701 (large scale), and CAN / ULC S109 (small and large scale). The product is approved by the Boston Fire Marshall (Cert.#39274), ULC (CR2702, CR2731), and ULI (R15076) registration has been completed. The product meets British Standards BS7837, BD5867 Part 2, and BD6341. On-going tests indicate approximately 80% strength retention after exposure equivalent to 2 years in Arizona.

FRAMEWORK
The framework of our shelters is made of 55,000 psi heavy-walled, galvanized tubing, an organic interior coating, and cold-rolled, high yield steel. Hot dipped uniform zinc coating. Chromate conversion. Daiwakeote acrylic clear coating. Wind load 70 mph.
More information at: http://www.ecpinfo.com/

FABRIC SPECIFICATIONS
WEAVE:	Nominal 16 by 22 ppi woven flame retardant HDPE scrim using natural FR / UV 1600 denier tapes
COATING:	2.75 mil. average each side
COLOR:	Off-white
WEIGHT:	11 ounce / yard
THICKNESS:	24 mils. – ASTM D5199

PERFORMANCE
GRAB TENSILE:	Warp 325 lb. 1445N	Weft 450 lb. 2000 N	ASTM D5034
TONGUE TEAR:	Warp 145 lb. 645N	Weft 140 lb. 622 N	ASTM D2261
MULLEN BURST:	730 psi 5037 kPa		ASTM D3786
ACCELERATED UV WEATHERING:	80% strength retention after 2000 hours QUV (A-340 lamps) 8 hours UV @ 60 degree C; 4 hours condensation @ 50 degree C		ASTM G53
LOW TEMPERATURE BEND:	Pass at 30 degree C (-22 degree F)		ASTM D522
FR & UV PERFORMANCE This product meets the requirements of CPAI-84 (1995) Sect. 5 and 6, ASTM E84 (Class 1), NFPA 701 (large scale), and CAN / ULC S109 (small and large scale). The product is approved by the Boston Fire Marshall (Cert.#39274), ULC (CR2702, CR2731), and ULI (R15076) registration has been completed. The product meets British Standards BS7837, BD5867 Part 2, and BD6341. On-going tests indicate approximately 80% strength retention after exposure equivalent to 2 years in Arizona.
FRAMEWORK The framework of our shelters is made of 55,000 psi heavy-walled, galvanized tubing, an organic interior coating, and cold-rolled, high yield steel. Hot dipped uniform zinc coating. Chromate conversion. Daiwakeote acrylic clear coating. Wind load 70 mph. More information at: http://www.ecpinfo.com/